卷 10, 期 8, 页码 1541-1548出版社
ELSEVIER
DOI: 10.1016/j.orgel.2009.08.024
关键词
Conjugated block copolymers; Transistor; Photovoltaic cell; Solvent; Surface structure
资金
- National Science Council
- Ministry of Economics Affairs of Taiwan
- NTU
- Japan Society for the Promotion of Science (JSPS) [20850014]
- Grants-in-Aid for Scientific Research [20850014] Funding Source: KAKEN
The electronic properties, morphology and optoelectronic device characteristics of conjugated diblock copolythiophene, poly(3-hexylthiophene)-block-poly(3-phenoxymethylthiophene) (P3HT-b-P3PT), are firstly reported. The polymer properties and structures were explored through different solvent mixtures of chloroform (CHCl3), dichlorobenzene (DCB), and CHCl3:DCB (1:1 ratio). The absorption maximum (lambda(max)) of P3HT-b-P311T prepared from DCB was around 554 nm with a shoulder peak indicative for the highly crystalline structure around 604 nm while that from CHCl3 was 516 nm without the clear shoulder peak. The field-effect hole mobility of P3HT-b-P3PT increased from similar to 6.0 x 10(-3), similar to 8.0 x 10(-3) to similar to 2.0 x 10(-2) cm(2) V-1 s(-1) as the DCB content in the solvent mixture enhanced. The AFM images suggested that the highly volatile CHCl3 processing solvent led to the amorphous structure, on the other hand, less volatile DCB resulted in the largely crystalline structure of the P3HT-b-P3PT. Such difference on the polymer structure and hole mobility led to the varied power conversion efficiency (PCE) of the photovoltaic cells fabricated from the blend of P3HT-b-P3PT/[6,6]-phenyl-C-61-butyric acid methyl ester (PCBM) (1:1, w/w): 1.88 (CHCl3), 2.13 (CHCl3:DCB (1:1)), and 2.60% (DCB). The PCBM blend ratio also significantly affected the surface structure and the solar cell performance. The PCE of polymer/PCBM could be improved to 2.80% while the ratio of polymer to PCBM went to 1:0.7. The present study suggested that the surface structures and optoelectronic device characteristics of conjugated diblock copolymers could be easily manipulated by the processing solvent, the block segment characteristic, and blend composition. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据