期刊
OPTICAL MATERIALS
卷 33, 期 11, 页码 1745-1752出版社
ELSEVIER
DOI: 10.1016/j.optmat.2011.06.010
关键词
Zirconia; Sub-micron particles; Luminescence; Europium; Erbium; Rare earth
Sub-micron sized crystalline particles of Eu3+ and Er3+-doped zirconia (ZrO2) were prepared via a wet chemical sol-gel route and post synthesis annealing. The doping was achieved by introduction of the respective rare earth salts into the zirconia precursor solution, with in situ generation of sodium chloride for stabilization of the particle surface during growth. A series of materials with differing europium content, nominally 0.3, 3 and 6 mol% within the ZrO2 lattice, were prepared for respective comparison and characterization of their optical properties following annealing at 700 degrees C. Average emission lifetimes of up to 2.3 ms were observed for the Eu3+-doped particles. Particle sizes, approximated from SEM micrographs, were observed in the range 250-400 nm. The synthesis of Er3+-doped ZrO2 particles (0.5 mol%) produced 300 nm sized particles which exhibited emission in the visible and infrared regions after annealing at 1000 degrees C. X-ray diffraction (XRD) with Rietveld analysis for phase quantification, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and photoluminescence (PL) spectra were used to characterize the samples. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据