期刊
SURFACE & COATINGS TECHNOLOGY
卷 275, 期 -, 页码 332-340出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2015.04.045
关键词
Tribological behavior; Columnar; Multilayered microstructure; Coefficient of friction; H/E
Multilayered CrN (M-CrN) coating was successfully prepared by arc ion plating method. The conventional CrN coatings were deposited under Ar + N-2 working pressures of 7.8 x 10(-1) Pa and 1.6 x 10(0) Pa, namely P-CrN and R-CrN respectively, for comparing the tribological behavior. M-CrN coating shows the multilayered microstructure. Transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) measurements evidenced the different stoichiometry between the P-CrN and R-CrN layers. The experimental results show that wear resistance of the M-CrN coatings was much better than that of the conventional CrN coatings. Instead of bulk flake-off behavior, wear mechanism of the M-CrN coating is the micro-area detachment. That is because the multilayered microstructure can inhibit the formation of cracks extended into the substrate, with the high hardness, low coefficient of friction and high H/E value. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据