SURFACE & COATINGS TECHNOLOGY
卷 276, 期 -, 页码 70-76出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2015.06.044
关键词
Chromium oxide coating; Deep oscillation magnetron sputtering (DOMS); High power impulse magnetron sputtering (HiPIMS); Crystallinity; Ion bombardment; Electron bombardment
The crystallinity of oxide phases strongly affects the properties of oxide coatings. In general, a well-crystallized oxide coating is desired because it usually results in improved mechanical and chemical properties. This paper presents a comparative study of the chromium oxide (Cr2O3) coatings deposited by deep oscillation magnetron sputtering (DOMS), mid-frequency pulsed dc magnetron sputtering (PDCMS) and continuous dc magnetron sputtering (DCMS) without applying external substrate heating. The DOMS-Cr2O3 coating deposition showed a peak substrate current density of 65 mA cm(-2) and a substrate saturation temperature of 250 degrees C, while the DCMS process exhibited a mean substrate current density of 1.29 mA cm(-2) and the lowest substrate saturation temperature of 212 degrees C. The sputtering techniques strongly affected the crystallinity of the Cr2O3 coatings. The DCMS-Cr2O3 coating exhibited an amorphous like structure. The PDCMS-Cr2O3 coating contained a mixture of amorphous and crystalline alpha-Cr2O3 phases. In contrast, the DOMS-Cr2O3 coating showed a strong crystallinity with a (110) preferential orientation. The improved crystallinity of the DOMS-Cr2O3 coating is attributed to the enhanced ion flux bombardment and a higher substrate saturation temperature, which is correlated to the energetic electron bombardment observed from the oscillatory substrate current. With the improved crystallinity, the DOMS-Cr2O3 coatings exhibited significantly improved mechanical properties (a hardness of 35 GPa) and wear resistance (a dry coefficient of friction of 0.37 and a wear rate of 5.7 x 10(-7) mm(3) N-1 m(-1)) as compared to the coatings deposited using DCMS and PDCMS. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据