SrTiO3 films; Spin coating; Ferroelectric properties; Ferromagnetism
资金
- National Natural Science Foundation of China [11032010, 11202054]
- Guangdong Provincial Educational Commission of China [2012KJCX0044]
The SrTi0.9Fe0.1O3-delta thin film grown on the LaNiO3 coated Si(100) substrates was prepared by a sol-gel process. The structure, micrograph, chemical states, electrical and magnetic properties of the thin film were investigated by using X-ray diffractometor (XRD), atomic force microscopy (ADM). X-ray photoelectron spectroscopy (XPS), ferroelectric test system and vibrating sample magnetometer (VSM), respectively. The results showed that the ferroelectric properties with the saturated polarization (2P(s)), remanent polarization (2P(r)) and coercive field (2E(c)) of 12.3 mu C/cm(2), 1.58 mu C/cm(2) and 33 kV/cm, respectively, at applied field of 200 kV/cm. The average remnant magnetization (M-r) and saturated magnetization (M-s) of the thin film were 3.74 x 10(-2) and 922 x 10(-2) emu/cm(3), respectively. Both the ferroelectric and ferromagnetic properties could be explained by the defect induced and the Fe ion substitution. Such multiferroic thin film was appropriate to be used in the field of multiferroic devices. (C) 2014 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据