Decoration of size-tunable CuO nanodots on TiO2 nanocrystals for noble metal-free photocatalytic H2 production

We report a simple yet effective approach for the decoration of the TiO2 nanocrystal surface with size-tunable CuO nanodots for high-performance noble metakfree photocatalytic H-2 production. Modification with polyacrylic acid enables the surface of TiO2 nanocrystals to be selectively deposited with Cu(OH)(2) nanodots, which can be subsequenty converted to CuO through dehydration without changing their morphologies. UV irradiation of the nanocomposite solution in the presence of a hole scavenger produces photogenerated electrons which reduce CuO to metallic Cu nanodots, making them effective co-catalysts in a role similar to Pt for promoting photocatalytic H-2 production. Due to the considerably high work function of Cu, the formation of a metal-semiconductor Schottky junction induces efficient charge separation and transfer. As a result, the TiO2 nanocrystals decorated with an optimal amount of CuO nanodots (1.7 wt%) could reach similar to 50% of the photocatalytic activity achievable by the Pt-TiO2 counterparts (1 wt%), clearly demonstrating the great potential of such composite catalysts for efficient noble metakfree photocatalytic H-2 production.