期刊
NANOSCALE
卷 4, 期 16, 页码 5202-5209出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c2nr30819c
关键词
-
类别
资金
- CSIR-Network [NWP0022, NWP-56]
- Council of Scientific and Industrial Research (CSIR) India
In the present investigation, hydrogen production via water splitting by nano-ferrites was studied using ethanol as the sacrificial donor and Pt as co-catalyst. Nano-ferrite is emerging as a promising photocatalyst with a hydrogen evolution rate of 8.275 mu mol h(-1) and a hydrogen yield of 8275 mu mol h(-1) g(-1) under visible light compared to 0.0046 mu mol h(-1) for commercial iron oxide (tested under similar experimental conditions). Nano-ferrites were tested in three different photoreactor configurations. The rate of hydrogen evolution by nano-ferrite was significantly influenced by the photoreactor configuration. Altering the reactor configuration led to sevenfold (59.55 mu mol h(-1)) increase in the hydrogen evolution rate. Nano-ferrites have shown remarkable stability in hydrogen production up to 30 h and the cumulative hydrogen evolution rate was observed to be 98.79 mu mol h(-1). The hydrogen yield was seen to be influenced by several factors like photocatalyst dose, illumination intensity, irradiation time, sacrificial donor and presence of co-catalyst. These were then investigated in detail. It was evident from the experimental data that nano-ferrites under optimized reaction conditions and photoreactor configuration could lead to remarkable hydrogen evolution activity under visible light. Temperature had a significant role in enhancing the hydrogen yield.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据