期刊
NANO LETTERS
卷 18, 期 9, 页码 5618-5627出版社
AMER CHEMICAL SOC
DOI: 10.1021/acs.nanolett.8b02092
关键词
Nanofriction; black phosphorus; chemical instability; degradation; lubrication
类别
资金
- National Natural Science Foundation of China [51475256, 51527901, 51811530014]
- Beijing Natural Science Foundation of China [3182010]
Due to its innate instability, the degradation of black phosphorus (BP) with oxygen and moisture was considered the obstacle for its application in ambient conditions. Here, a friction force reduced by about 50% at the degraded area of the BP nanosheets was expressly observed using atomic force microscopy due to the produced phosphorus oxides during degradation. Energy-dispersive spectrometer mapping analyses corroborated the localized concentration of oxygen on the degraded BP flake surface where friction reduction was observed. Water absorption was discovered to be essential for the degraded characteristic as well as the friction reduction behavior of BP sheets. The combination of water molecules as well as the resulting chemical groups (P-OH bonds) that are formed on the oxidized surface may account for the friction reduction of degraded BP flakes. It is indicated that, besides its layered structure, the ambient degradation of BP significantly favors its lubrication behavior.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据