期刊
METALS AND MATERIALS INTERNATIONAL
卷 19, 期 5, 页码 999-1004出版社
KOREAN INST METALS MATERIALS
DOI: 10.1007/s12540-013-5012-4
关键词
deformation; texture; twinning; electron backscattered diffraction (EBSD)
资金
- World Premier Materials (WPM) Program
- Korea Ministry of Knowledge Economy through the Research Institute of Advanced Materials
In order to investigate tensile twinning behavior, the magnesium single crystal was deformed by compressing along the direction at room temperature, as tensile twinning easily takes place when the compression direction is perpendicular to the c-axis. Numerous primary tensile twins were activated during deformation, and the Schmid factor (SF) criterion was applied to the six twin variants. The analysis shows that the majority of the primary twins belong to high SF variants, and high SF twin boundaries provided nucleation sites for low SF variants. The secondary tensile twins were formed inside the high SF of wide primary twin bands, and the basal plane of the secondary twin was tilted about 60A degrees with respect to the original parent matrix. In the case of the secondary tensile twin, relatively low SF variants were activated while counterparts with higher SF variants were absent.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据