关键词
Cu alloy; precipitate; electrical conductivity; tensile property
资金
- Ministry of Knowledge Economy, Republic of Korea
The electrical conductivity of Cu-P based sheet alloys tended to decease with increase of the total amount of final cold rolling, while alloy tensile strength proportionally increased. When the cold rolling was carried out at an extremely low temperature, the tensile strength was more remarkably increased, even though the degree of reduced conductivity was generally similar to that found in the ordinary cold rolling process. It is well known that strain hardening reduces the electrical conductivity of pure Cu and Cu alloys; however, in this work it is reported that the degree of reduction is apparently larger than previously thought. TEM analysis revealed that various fine P-containing precipitates were formed in the experimental alloys. The unstable interface between the coarse P-containing precipitates and the Cu matrix is postulated to be responsible for the significant drop of conductivity.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据