METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
卷 43A, 期 13, 页码 5182-5192出版社
SPRINGER
DOI: 10.1007/s11661-012-1341-z
关键词
-
资金
- Ministry of Education, Culture, Sports, Science and Technology (MEXT) of Japan
- Light Metals Educational Foundation of Japan
- Ministry of Education, Culture, Sports, Science and Technology of Japan in the Innovative Area Bulk Nanostructured Metals
- Kyushu University
Al-Fe alloys in the form of thin disks 10 mm in diameter, with Fe nominal weight fractions of 0.5, 1, 2, and 5 pct, were extracted from bulk-extruded rods and processed by high-pressure torsion (HPT). A group of these bulk samples was processed in an as-received state, whereas another group was annealed at 773 K (500 A degrees C) for a period of 1 hour, prior to the application of HPT. An additional set of samples was prepared by mixing high-purity powders with similar Fe contents and consolidated directly in the HPT facility. The samples were processed up to 10 revolutions. Vickers microhardness, tensile strength, and elongation to failure were evaluated for all cases along with observations of the Al matrix by transmission electron microscopy (TEM). Basic characterization of the microstructures was carried out by X-ray diffraction (XRD) and optical microscopy (OM). Significant strengthening with ductility retained was achieved in the bulk samples as a consequence of grain refinement and dispersion of intermetallic phases. Powder samples had a more gradual increase in strength but increased ductility as a result of the imposed strain.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据