Cast specimens of Mg and of several Mg-Zn binary alloys with a wide range of grain sizes were deformed in tension and compression. The k values calculated from the Hall-Petch (H-P) plots of the tensile 0.2 pct proof stress increased with the Zn content, from 0.24 MPa m(1/2) for pure Mg to similar to 0.66 MPa m(1/2) for the 2.3 at. pct Zn alloy; k values measured from compression tests were larger, typically by 0.05 MPa m(1/2). When the strength measurements were corrected for the pseudoelastic strain resulting from elastic twinning, the k values generally increased, and the difference between tension and compression was eliminated. This showed that the larger k values obtained in compression using uncorrected data were an artifact of the pseudoelastic effect. The apparent friction stress varied between about 14 MPa for pure Mg to very low or negative values for the most dilute alloy, increasing again to about 8 MPa for the most concentrated alloy. The use of strength data corrected for pseudoelasticity effects is necessary for a consistent analysis of the grain size hardening.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据