The Effect of Friction Stir Processing on the Mechanical Properties of Investment Cast and Hot Isostatically Pressed Ti-6Al-4V

Friction-stir (FS) processing was used to modify the coarse, fully lamellar microstructure of investment cast and hot isostatically pressed (HIP'ed) Ti-6Al-4V. The effect of FS processing on mechanical properties was investigated using microtensile and four-point bend fatigue testing. The tensile results showed a typical microstructure dependence where yield strength and ultimate tensile strength both increased with decreasing slip length. Depending on the processing parameters, fatigue strength at 10(7) cycles was increased by 20 pct or 60 pct over that of the investment cast and HIP'ed base material. These improvements have been verified with a statistically significant number of tests. The results have been discussed in terms of the resistance of each microstructure fatigue crack initiation and small crack propagation. For comparison, a limited number of fatigue tests was performed on alpha + beta forged Ti-6Al-4V with varying primary alpha volume fraction and also on investment cast material heat treated to produce a bi-lamellar condition.