METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
卷 41A, 期 1, 页码 61-72出版社
SPRINGER
DOI: 10.1007/s11661-009-0069-x
关键词
-
资金
- CICYT [MAT2003-01172, MAT2006-11202]
- Spanish National Research Council (CSIC)
Two aluminum multilayer laminates have been processed by hot roll bonding following similar processing paths. The first one is constituted by alternated Al 2024 and Al 1050 layers (ALH19) and the second one by alternated Al 7075 and Al 1050 layers (ADH19). The influence of the constituent materials in the multilayer laminates both during the processing at high temperature and during the subsequent mechanical characterization has been analyzed. The mechanical behavior of the as-received materials at the processing conditions has been characterized by hot torsion. Multilayer laminates have been tested at room temperature under impact Charpy tests, three-point bend tests, and shear tests on the interfaces. The relative toughness increase compared to the constituent materials was much higher for the ADH19 laminate based on the high-strength Al 7075 alloy than for the ALH19 laminate. This is attributed to the different fracture mechanism.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据