期刊
MATERIALS TRANSACTIONS
卷 59, 期 10, 页码 1610-1615出版社
JAPAN INST METALS
DOI: 10.2320/matertrans.M2018055
关键词
densification; grain growth; polycrystalline Al2O3; two-step pulsed electric current sintering
In this study, transparent polycrystalline Al2O3 with a diameter of 30mm was fabricated by two-step pulsed electric current sintering (TS-PECS) at two different heating rates, 100 and 10 degrees C/min. The overall TS-PECS process was divided into parts and was stopped at various positions along the timeline. The relative density and grain size of the Al2O3 samples obtained from each stop were evaluated. In general, the results show that the heating rate changed the densification rate in each sintering stage but did not strongly affect the final density. However, it dramatically influenced the grain growth of Al2O3. With the higher heating rate, the dynamic grain growth was assumed to enhance the grain growth rate because of the high concentration of defects, especially in the last stage of sintering. Especially, a grain size refinement phenomena was observed during the sintering process of polycrystalline Al2O3 for the first time.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据