期刊
MATERIALS SCIENCE IN SEMICONDUCTOR PROCESSING
卷 16, 期 3, 页码 868-876出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.mssp.2013.01.012
关键词
Nanowire; Cathodic electrodeposition; Manganese (IV) oxide; Supercapacitor
One-dimensional manganese (IV) oxide (MnO2) (similar to 20 nm in average diameter) were synthesized by cathodic electrodeposition and heat treatment. The mechanism of electrodeposition and nanowire formation were discussed. The product was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Fourier transform infrared (FT-IR). Nanowires with varying lengths and diameters were found in TEM and SEM images of the sample. The results of N-2 adsorption-desorption analysis indicated that the BET surface area of the MnO2 nanowires was 157 m(2) g(-1) and the pore size distributions were 2.5 and 4.5 nm. The electrochemical performances of the prepared MnO2 as an electrode material for supercapacitors were evaluated by cyclic voltammetry and galvanostatic charge/discharge measurements in a solution of 0.5 M Na2SO4. The higher specific capacitance of 318 F g(-1) and good capacity retention of 86% were achieved after 1000 charge-discharge cycles had been observed for the MnO2 nanowires electrode. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据