DOI: 10.1016/j.msea.2014.06.006
关键词
Hot deformation; Titanium alloy; Processing map; Dynamic recovery; Dynamic recrystallization
Hot deformation characteristic of Ti-5Al-5V-5Mo-3Cr alloy with a starting microstructure of an equiaxed single beta microstructure is examined in relation to microstructural evolution and the result according to processing map technique. In testing at 700 degrees C, subgrain formation is dominant at higher strain rate, while superplasticity occurs at lower strain rate. Herein, dynamic alpha precipitation from supersaturated beta phase occurs during deformation and affects the flow behavior. In testing at and above 800 degrees C, dynamic recovery (DRV) is dominant and continuous dynamic recrystallization (CDRX) also occurs especially in the vicinity of boundaries of prior-beta-grains. There are three domains having an optimized power dissipation efficiency (ranging from 40% to 50%) in processing map. These three domains are reasonably explained in relation to microstructural conversion of frequent activations of grain boundary sliding, dynamic recovery and simultaneous occurrence of dynamic recovery and continuous dynamic recrystallization. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据