Steel; Martensite; Synchrotron X-ray diffraction; Tensile deformation
类别
资金
- Research Program of the Materials innovation institute M2i [M41.5.08313]
The stability of individual metastable austenite grains in low-alloyed TRIP steels has been studied during tensile loading using high-energy X-ray diffraction. The carbon concentration, grain volume and grain orientation with respect to the loading direction was monitored for a large number of individual grains in the bulk microstructure. Most austenite grains transform into martensite in a single transformation step once a critical load is reached. The orientation-dependent stability of austenite grains was found to depend on their Schmid factor with respect to the loading direction. Under the applied tensile stress the average Schmid factor decreased from an initial value of 0.44 to 0.41 at 243 MPa. The present study reveals the complex interplay of microstructural parameters on the mechanical stability of individual austenite grains, where the largest grains with the lowest carbon content tend to transform first. Under the applied tensile stress the average carbon concentration of the austenite grains increased from an initial value of 0.90 to 1.00 wt% C at 243 MPa, while the average grain volume of the austenite grains decreased from an initial value of 19 to 15 mu m(3) at 243 MPa. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据