Microstructure, tensile properties and fracture behavior of high temperature Al-Si-Mg-Cu cast alloys

The high temperature tensile behavior of 354 aluminum cast alloy was investigated in the presence of Zr and Ni. The cast alloys were given a solutionizing treatment followed by artificial aging at 190 degrees C for 2 h. High temperature tensile tests were conducted at various temperatures from 25 degrees C to 300 degrees C. Optical microscopy and electron probe micro-analyzer were used to study the microstructure of different intermetallic phases formed. The fractographic observations of fracture surface were analyzed by scanning electron microscopy to understand the fracture mechanism. The results revealed that the intermetallics phases of (Al, Si)(3)(Zr, Ti), Al3CuNi and Al9NiFe are the main feature in the microstructures of alloys with Zr and Ni additions. The results also indicated that the tensile strength of alloy decreases with an increase in temperature. The combined addition of 0.2 wt% Zr and 0.2 wt%, Ni leads to a 30% increase in the tensile properties at 300 degrees C compared to the base alloy. Zr and Ni bearing phases played a vital role in the fracture mechanism of the alloys studied. Crown Copyright (C) 2013 Published by Elsevier B.V. All rights reserved.