期刊
出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2013.04.099
关键词
Selective laser melting; Hot isostatic pressing; Titanium alloys; Microstructure; Tensile behaviour
类别
资金
- Technology Strategy Board (TSB), UK
- Rolls-Royce, plc
Ti-6Al-4V samples have been prepared by selective laser melting (SLM) with varied processing conditions. Some of the samples were stress-relieved or hot isostatically pressed (HIPed). The microstructures of all samples were characterised using optical microscopy (OM), scanning electron microscopy (SEM) and X-ray diffraction (XRD) and the tensile properties measured before and after HIPing. It was found that the porosity level generally decreased with increase of laser power and laser scanning speed. Horizontally built samples were found to have a higher level of porosity than vertically built samples. The as-fabricated microstructure was dominated by columnar grains and martensites. HIPing closed the majority of the pores and also fully transformed the martensite into alpha and beta phases. The asfabricated microstructure exhibits very high tensile strengths but poor ductility with elongation generally smaller than 10%. The horizontally built samples show even lower elongation than vertically built samples. HIPing considerably improved ductility but led to a reduction in strength. With HIPing, the SLMed samples were found to show tensile properties comparable with those thermomechanically processed and annealed samples. Crown Copyright (c) 2013 Published by Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据