Friction stir spot welding; Fatigue; Magnesium alloy
类别
资金
- USAMP Magnesium Front End RD Project [DE-EE0003583]
- Department of Energy and the National Energy Technology Laboratory [DE-FC26-02OR22910]
- agency of the United States Government
In this paper the fatigue behavior of the friction stir spot welded (FSSW) coupons of magnesium AZ31 alloy manufactured under different welding process conditions is investigated. Two sets of lap-shear coupons were made based on variation in plunge depth, tool rotation speed and tool geometry. Metallographic analysis of the untested FSSW coupons revealed differences in weld geometry and microstructure. Interfacial hooking of the faying surface was found to vary significantly between the two sets of process conditions. Microhardness test data revealed a large gradient in hardness profile. Results from the load controlled cyclic tests showed that lower tool rotation and shallower shoulder plunge depth led to better fatigue performance. Optical fractography of the fatigued coupons revealed that fatigue cracks initiated at the weld interface in both sets of coupons. However, the fracture mode showed variability between the two process conditions. The fractography analysis suggests that the effective top sheet thickness, interfacial hook and microstructure, which are largely determined by the process conditions, significantly affect the fatigue behavior of the friction stir spot welds in magnesium alloys. (c) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据