Characterisation of high pressure torsion processed 7150 Al-Zn-Mg-Cu alloy

出版社

ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2012.05.026

关键词

7150 Al-Zn-Mg-Cu alloy; High pressure torsion (HPT); Hardness measurement; Electron microscopy; Differential scanning calorimetry and electrochemical behaviour

资金

  1. National Institute of Technology, Durgapur, India

向作者/读者索取更多资源

Solution treated 7150 Al-Zn-Mg-Cu alloy samples were subjected to high pressure torsion (HPT) at room temperature and artificial ageing. Microhardness of HPT processed samples increases with distance from the centre, saturating near the edge of the disk. The hardness obtained through riff processing is higher compared to that obtained by conventional solution treatment and artificially ageing of this high strength aluminium alloy. Differential scanning calorimetry (DSC) and transmission electron microscopy (TEM) revealed the sequence of solid state reactions occurring in the Al-Zn-Mg-Cu system, and the presence of beta' (Al3Zr), eta'(MgZn2) and eta (MgZn2) phases, respectively. TEM of HPT processed samples revealed that the grains near the edge of the disk are finer compared to that near the centre of the disk. Electrochemical polarisation studies of the HPT processed 7150 alloy indicated open circuit potential (OCP) and corrosion potential (E-corr) values are more negative (i.e. anodic), and corrosion current density (i(corr)) values are about one order higher than the values of artificially aged tempers. (C) 2012 Elsevier B.V. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据