MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 528, 期 19-20, 页码 6121-6127出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2011.03.115
关键词
Ni-based superalloy; Inconel 740; Nanoindentation; Precipitation strengthening; Aging
类别
资金
- Korea government Ministry of Knowledge Economy [20101020300460]
- Korea Evaluation Institute of Industrial Technology (KEIT) [20101020300460] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
Influence of isothermal aging on the microstructures and hardness in Inconel 740, a relatively new Ni-based superalloy, was explored using the specimens aged at 810 degrees C for different times. As aging time increased, the size of gamma prime precipitates continuously increased while their fraction remained almost constant. Nanoindentation experiments revealed that the overall hardness increased till the aging time of 100 h and then decreased with the aging time. Estimation of phase hardness by applying a simple rule-of-mixture showed that, with aging time, the hardness of gamma matrix decreased whereas that of gamma prime precipitates increased. The aging-induced strength change is discussed in terms of the possible contributions of precipitation strengthening and solid solution strengthening. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据