MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 528, 期 16-17, 页码 5627-5635出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2011.03.095
关键词
Magnesium alloy; Electropulsing treatment; Recrystallization; Mechanical properties
类别
资金
- National Natural Science Foundation of China [50571048]
- City University of Hong Kong [7002303]
Influences of electropulsing treatment (EFT) on microstructure and mechanical properties of cold-rolled Mg-9Al-1Zn alloy strip were studied. EPT was found to accelerate the recrystallization of cold-rolled Mg-9Al-1Zn alloy strip at a relatively low temperature, and obtain fine microstructure of quasi-single-phase-recrystallized grains. The EPT-induced microstructural changes weakened the intensity of the basal fiber texture, and increased elongation to failure remarkably with a decrease in tensile strength. Fracture surface analysis showed that transition from intergranular brittle facture to transgranular dimple fracture took place with an increase in frequency of EPT. The rapid recrystallization behaviour of the Mg-9Al-1Zn alloy strip under EPT was attributed to the enhancement of nucleation rate and atomic diffusion resulting from the coupling of the thermal and athermal effects. It is supposed that EFT can provide a highly efficient method for the intermediate-softening annealing of magnesium alloys sheet/strips. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据