MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 528, 期 3, 页码 1534-1539出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2010.11.003
关键词
Superalloy; Carbides; Grain boundary; Stress-rupture properties
IN792 alloy containing different C contents (0.016-0.21%) was refined in vacuum induction melting furnace. The morphology, size and area fractions of gamma' and carbides were investigated with change of C contents in alloys from 0.016% to 0.21%. No variations were observed in morphology and size of gamma' phase, and very small variation of area fraction of gamma' was observed in alloys with different C contents. The area fractions of carbides varied from 1.10% to 2.72% among alloys with different C contents. When C contents were in range of 0.05-0.14%, the small size carbide particles of MC and M23C6 were prone to appear. When C contents were in range of 0.13-0.21%, the large size of carbide particles formed in grain boundary with film and big block. With increasing C content, the stress-rupture lives of specimens increased in the range of 0.016-0.086% and decreased in the range of 0.086-0.14%, but they did not change when the C contents was above 0.14%. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据