MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 527, 期 13-14, 页码 3253-3258出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2010.02.031
关键词
Nb-based alloy; Silicides; Mechanical alloying; Fracture toughness
类别
资金
- National Natural Science Foundation of China [50775052]
Nb-16 at.% Si bulk alloys were fabricated by hot pressing from compound powders milled for different times. The influences of mechanical alloying on microstructure and mechanical properties of the hot-pressed alloys were investigated. The results indicate that the particle size of powders was significantly refined and the addition of absolute ethyl alcohol suppressed the agglomeration of powders. When milling time increased from 6 to 24 h, the constituent phases (Nbss, Nb5Si3 and Nb3Si) changed from large size trips to fine near-equiaxed shape, and the volume fraction of ductile Nbss decreased. In addition, Vickers hardness and flexural strength of bulk alloys increased gradually owing to the enhancement of the volume fraction of niobium silicides. Fracture toughness was in range of 10.98-13.23 MPa m(1/2), which was higher than that of cast materials. It was attributed to the positive role of ductile phase and fine-grain toughening. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据