The processing and mechanical behavior of Al2O3 composites with 1-20 wt.% nano-/micro-sized SiC particles was investigated. The composites were densified by hot-pressing. The mechanical properties of nano-/micro-sized SiC/Al2O3 composites including hardness, fracture toughness and flexural strength were investigated. It was found that the fracture strength and fracture toughness of the nano-/micro-sized SiC/Al2O3 composites were significantly improved in comparison with the monolithic Al2O3.7.6 MPa m(1/2) was the highest fracture toughness and was found in the composite with 5% SiC, while the 20% Sic composite exhibited the highest flexural strength. The toughening and strengthening mechanisms of the ceramic composites were discussed. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据