For massive brittle materials, the fracture toughness in mode 1, K-IC, can be determined using various reliable techniques. Besides, Vickers Indentation Fracture (VIF) technique has been developed to locally determine fracture toughness. However, since the indentation test generates a complex three-dimensional crack system around the indent, fracture toughness, K-C, is calculated instead of K-IC. Consequently some authors rightly reject the VIF technique to determine standard fracture toughness by arguing that the literature counts numerous VIF crack equations thus revealing discrepancies of this technique. Nevertheless in some cases (e.g. brittle ceramic coatings) inclusive material techniques are not applicable since presence of the substrate and/or multi-crack network can modify the crack propagation into the coating. In this work, we employed VIF technique to study multi-cracking behavior of titania, alumina and zirconia ceramic oxide coatings obtained by plasma spraying. To calculate VIF toughness, we propose (i) to select two crack equations for radial-median and Palmqvist cracking modes respectively, (ii) to adjust the crack equation of Miranzo and Moya for intermediate cracking mode. (iii) to develop a mathematical approach to determine the cracking mode, (iv) to take into account the multi-crack network by defining an equivalent four-crack system and (v) to propose a universal crack equation applicable independently of the cracking mode. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据