MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 478, 期 1-2, 页码 351-360出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2007.06.025
关键词
aluminium alloy; 7xxx; friction stir welding; microstructure; SAXS
In order to improve the efficiency of the friction stir welding (FSW) manufacturing process a recently developed 7xxx series aluminium alloy has been welded in an underaged temper for age forming (TAF) condition and subsequently heat treated to the required T7 in service temper. Several complementary microstructural measurement techniques (SEM, TEM and SAXS) have been employed to capture a detailed view of the precipitate distribution, mean particle size, phase identity and fraction. Each friction stir weld zone has been treated separately and compared with the original underaged structure to capture the effect of the local thermal history. A comparison is made between microstructural measurements and predictions of the equilibrium fraction and solvus temperature for each phase using a CALPHAD approach. In contrast with welding thin sections the cooling rates obtained after friction stir welding thick plate are slow enough to allow precipitation of eta'/eta-phase within the nugget and TMAZ on cooling of the weld, at both grain boundaries and throughout the grain interior. Applying a subsequent post-weld heat treatment in effect replaces the fine -eta'/eta-phase with coarse overaged precipitates in the nugget/TMAZ and reduces the strength contrast between nugget/TMAZ and HAZ. (c) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据