MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 491, 期 1-2, 页码 434-439出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2008.02.028
关键词
duplex stainless steel; cyclic behavior; dislocation structure; embrittlement; dynamic strain aging; high temperature
The cyclic behavior of type UNS S32750 (super) duplex stainless steels (DSSs) in as-received and aged conditions was investigated between room temperature and 500 degrees C. The pronounced cyclic hardening observed in as-received samples between 200 and 475 degrees C is associated with the activation of dynamic strain aging (DSA) in the ferritic phase. On the other hand, during the entire fatigue life aged samples only show a cyclic softening behavior that could be related to the demodulation of the spinodal decomposition in the ferrite phase. It is worthwhile to point out that despite the manifestation of DSA in as-received samples at intermediate temperatures and the presence of spinodal decomposition in aged samples no influence of these phenomena on the fatigue lifetime was observed. (c) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据