MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 498, 期 1-2, 页码 321-326出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2008.08.008
关键词
SiO2 glass ceramic; Brazing; Microstructure; Mechanical properties
类别
资金
- National Natural Foundation of Science [50705022]
- Harbin Institute of Technology
In this paper, SiO2 glass ceramic was brazed to Ti-6Al-4V alloy with a commercially available AgCuTi filler foil as braze alloy. Various brazing heating cycles were Carried out to study the effects of brazing parameters on the joint interface and mechanical properties. The experimental result shows that the typical interface structure of the joints is SiO2/TiSi2 + Ti4O7/TiCU + Cu2Ti4O/Ag(s.s) + Cu(s.s)/TiCu/Ti2Cu/Ti + Ti2Cu/Ti-6Al-4V from SiO2 glass ceramic to Ti-6Al-4V alloy side. The microstructure of the brazed joint is related to the solution and chemical reaction among atoms during the brazing. According to the mechanical property tests, the joint brazed at 900 degrees C for 5 min obtains the maximum shear strength 27 MPa. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据