Use of Ni-Zn Ferrites Doped with Cu as Catalyst in the Transesterification of Soybean Oil to Methyl Esters

The purpose of this work is to evaluate the performance of Ni0.5Zn0.5Fe2O4 ferrite doped with 0.1 and 0.4 mol of Cu as a catalyst for the transesterification of soybean oil to biodiesel, using methanol. The samples were characterized by X-ray diffraction, nitrogen adsorption and scanning electron microscopy. The reaction was performed for 2 hours at a temperature of 160 degrees C, using 10 g of soybean oil, a molar ratio of oil: alcohol of 1:20, and 4% (w/w) of catalyst. The product of the reaction was characterized by gas chromatography, which confirmed conversion to methyl esters. The diffraction patterns showed the presence only of Ni0.5Zn0.5Fe2O4 ferrite phase with a crystallite size of 29 nm. The samples doped with 0.1 and 0.4 mol of Cu showed a surface area and particle size of 22.17 m(2)g(-1) and 50.47 nm; and 23.49 m(2)g(-1) and 47.64 nm, respectively. The morphology of both samples consisted of brittle block-shaped agglomerates with a wide particle size distribution. A comparative analysis of the two catalysts indicated that the catalyst doped with 0.4 mol of Cu showed the better performance, with a conversion rate of 50.25%, while the catalyst doped with 0.1 mol of Cu showed 42.71% conversion.