Template synthesis of low-density gold foams: Density, microstructure and compressive strength

期刊

MATERIALS RESEARCH BULLETIN
卷 48, 期 9, 页码 3499-3504

出版社

PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.materresbull.2013.05.035

关键词

Structural materials; Chemical synthesis; Mechanical properties; Microstructure

资金

  1. National Natural Science Foundation of China (NNSFC) [51202203]
  2. State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials (Southwest University of Science and Technology) [11zxfk26]
  3. China Postdoctoral Science Foundation [2012M520078]

向作者/读者索取更多资源

High Z metallic foams with low density are required in high energy-density physical experiments. In this study, cylindrical Au foams with relative density as low as 5.6% were synthesized from a templating approach. Microspherical polystyrene (PS) was employed as the sacrificial template and aqueous solution of HAuCl4 as gold source. Au nanoparticles were successfully coated onto the surface of PS template from a two-step deposition process. Cylindrical PS/Au monoliths were formed by filter-casting of the Au coated PS beads. PS template was completely removed and self-supported Au foams were produced after drying, demolding and calcination. The monolithic Au foams demonstrate density as low as 1.08 g/cm(3) and compressive strength as high as 3.2 Mpa. (C) 2013 Elsevier Ltd. All rights reserved.