期刊
MATERIALS RESEARCH BULLETIN
卷 44, 期 6, 页码 1232-1237出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.materresbull.2009.01.009
关键词
Nanostructures; Crystal growth; Catalytic properties
资金
- National Science Foundation of China [50425415, 50772004]
- National Basic Research Program of China (973 Program) [2007CB613608]
Large-scale, well-aligned single crystalline TiO2 nanorod arrays were prepared on the pre-treated glass substrate by a hydrothermal approach. The as-prepared TiO2 nanorod arrays were characterized by Xray diffraction, scanning electron microscopy and transmission electron microscopy. X-ray diffraction results show that the main phase of TiO2 is rutile. Scanning electron microscopy and transmission electron microscopy results demonstrate that the large-scale TiO2 nanorod arrays grown on the pre-treated glass substrate are well-aligned single crystal and grow along [001] direction. The average diameter and length of the nanorods are approximately 21 and 400 nm, respectively. The photocatalytic activity of TiO2 nanorod arrays was investigated by measuring the photodegradation rate of methyl blue aqueous Solution under UV irradiation (254 nm). And the results indicate that TiO2 nanorod arrays exhibit relatively higher photocatalytic activity. (C) 2009 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据