Synthesis, characterization and humidity sensing properties of Cu-Sr-Al mixed metal oxide composites

期刊

MATERIALS RESEARCH BULLETIN
卷 43, 期 2, 页码 473-482

出版社

PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.materresbull.2007.02.030

关键词

ceramics; composites; oxides; sol-get chemistry; X-ray diffraction

向作者/读者索取更多资源

Copper-strontium-aluminum mixed metal oxide composites prepared by sol-gel technique was investigated for humidity sensing properties. X-ray diffraction, scanning electron microscopy (SEM), FT-IR spectroscopy and nitrogen adsorption/desorption isotherm at 77 K was employed, respectively, to identify the structural phases, surface morphology, vibrational stretching frequencies and BET surface area of the composites. The composites were prepared with the mole ratios of Cu:Sr as (0.0:1.0, 0.2:0.8, 0.4:06, 0.6:0.4, 0.8:0.2 and 1.0:0.0) keeping the aluminium mole ratio as constant and were labeled as CuSA1, CuSA2, CuSA3, CuSA4, CuSA5 and CuSA6, respectively. The samples sintered at 900 degrees C for 5 h, were subjected to dc resistance measurements as a function of relative humidity (RH) in the range 5-98% and the results revealed that the sensitivity factor of CuSA5 possessed the highest humidity sensitivity of 42,000 while the pure composite copper aluminate (CuSA1) and strontium aluminate (CuSA6) possessed comparatively low sensitivities 10,000 and 20,000, respectively. The response and recovery characteristics of the composites CuSA1, CuSA5 and CuSA6 were studied. (C) 2007 Elsevier Ltd. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据