关键词
Silicon carbide; Aerogel; Carbothermal reduction; Sol-gel process; Porous materials
资金
- Priority Academic Program Development of Jiangsu Higher Education Institution (PAPD)
- Program for Changjiang Scholars and Innovative Research Team in University (PCSIRT)
Resorcinol-formaldehyde/silica composite (RF/SiO2) gels were synthesized in one pot using a facile process. RF/SiO2 aerogels were obtained after supercritical carbon dioxide fluid drying. Monolithic mesoporous silicon carbide (SiC aerogels) was prepared from RF/SiO2 aerogels after carbothermal reduction and calcination. The as-prepared SIC products exhibited monolithic mesoporous morphology and possessed a BET specific surface area of 251 m(2)/g and a pore volume of 0.965 cm(3)/g. X-ray diffraction (XRD) and transmission electron microscopy (TEM) demonstrated that the resulting SiC aerogels were composed of alpha-SiC nanocrystals. The bulk density and skeleton density of SiC products is 0.288 g/cm(3) and 3.12 g/cm(3), respectively. The porosity of SiC products is 90.8%. The SiC aerogels were stable up to temperatures near 650 degrees C. (c) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据