MATERIALS LETTERS
卷 91, 期 -, 页码 55-58出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.matlet.2012.09.060
关键词
Multiferroics; Nanofibers; Nanocomposites; Sol-gel preparation; Electrospinning
资金
- State Key Laboratory of Advanced Welding and Joining
- Harbin Institute of Technology
The multiferroic Ba0.7Sr0.3TiO3 (BSTO)-Ni(0.8)Zna(2)Fe(2)O(4) (NZFO) nanofibers with different molar ratios were prepared by electrospinning method. After annealing at 700 degrees C, the composite nanofibers showed highly crystalline structure with no impurity phase. The fibers before and after heat treatment had high aspect ratios, and the fibrous morphology could be observed obviously. The maximum value of magnetic coercivity was obtained corresponding to the BSTO-NZFO nanofibers with molar ratio of 80/20. The values of coercivity, saturation magnetization and retentivity for the BSTO-NZFO (molar ratio=80/20) nanofibers were 44.873 Oe, 2.479 emu/g and 0.189 emu/g, respectively. Moreover, the magnetodielectric, dielectric and ferroelectric properties were measured at room temperature. (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据