期刊
MATERIALS LETTERS
卷 76, 期 -, 页码 55-58出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.matlet.2012.02.064
关键词
Electrodeposition; Energy storage and conversion; Thin films
资金
- National Science Foundation of China (NSFC) [20903031]
- Development Program for Outstanding Young Teachers
- Fundamental Research Funds for the Central University [HIT. NSRIF. 2010 056]
- State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology [QA201026]
Si film was prepared by electrodepositing on Ni substrate. SEM images and EDS analysis illustrated that the Si film was obtained successfully. The Si film anodes displayed a high reversible specific capacity (over 2800 mAhg(-1)), an excellent stability (little fading after 80 cycles at a current of 0.36 Ag-1, corresponding to 0.1 C), high rate performances (850 mAhg(-1) at a current of 18 Ag-1, corresponding to 5 C) and high electrochemical stability (The capacity was still more than 2600 mAhg(-1), when the current density returned to 0.36 Ag-1 after cycling at the high current densities). Electrochemical impedance spectroscopy tests showed that the Li+ diffusion coefficient of the Si film was much higher than the pristine Si nanoparticles, which resulted in the high rate performances of the Si film. (C) 2012 Elsevier BM. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据