Ferroelectric; Dielectric; Thick films; KNN-BT; Aerosol deposition (AD); Hardening
资金
- Ministry of Knowledge Economy, Republic of Korea
- Korea Evaluation Institute of Industrial Technology (KEIT) [K0004114] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
Highly dense, 30 mu m-thick 0.95(K0.5Na0.5)NbO3-0.05BaTiO(3) (KNN-BT) lead-free films were successfully fabricated on alumina substrate by aerosol deposition (AD) and the effect of Mn doping (0 mol%, 0.5 mol% and 1.0 mol%) on the film properties was investigated. It was found that low field dielectric constant decreases by 36% for 0.5 mol% Mn doping and 42% for 1 mol% Mn doping. The loss factor was found to reduce by 19% for 0.5 mol% Mn doping and 43% for 1 mol% Mn doping. Based on the high field polarization-electric field measurement, we demonstrate that Mn induces hardening in KNN-BT thick films. The hardening is believed to be due to the pinning of the domains by dipolar defects at domain boundaries. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据