关键词
Composite materials; Sintering; Electrochemical techniques; Electrochemical properties
资金
- key item of Mineral Resources Chemistry Key Laboratory of Sichuan Higher Education Institutions [KZH201103]
- Cultivating programme of Middle-aged backbone teachers [HG0092]
- Chengdu University of Technology [HY0084]
- Sichuan Province [SZH1106CX04]
Rh-doped LiNi0.5Mn1.5O4 has been prepared for the first time as the 5 V cathode materials of lithium ion batteries. The samples were characterized by X-ray diffraction, scanning electron microscopy, inductively coupled plasma analysis and electrochemical measurements. The results indicated that the rate capability and cycling stability of LiNi0.5Mn1.5O4 at 25 and 55 degrees C was effectively improved by doping with 2 mol% Rh. At a 3000 mA g(-1) (20 degrees C) charge/discharge rate, the LiNi0.48Rh0.02Mn1.5O4 sample still delivered an initial discharge capacity of 92.4 mAh g(-1) at 25 degrees C. Furthermore, it maintained 83.6% of its initial capacity after 300 cycles under a 150 mA g(-1) current rate (1 degrees C) at 55 degrees C. These improvements were principally attributed to Rh-substitution, which not only enhanced the electronic conductivity and lithium ion diffusion ability of LiNi0.5Mn1.5O4, but also suppressed the destruction of electrolyte during cycling. The thermal stability of LiNi0.5Mn1.5O4 was also enhanced by Rh-doping. (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据