LaFeO3; Glucose; Sol-gel process
资金
- Natural Science Foundation of China [10975055]
LaFeO3 were prepared by sol-gel process using glucose as a complexing agent. Thermogravimetric (TG), differential thermal analysis (DTA), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), Field emission scanning electron microscope (FSEM) and Transmission electron microscope (TEM) techniques were used to characterize precursor and derived oxide powders. The effect of the mol ratios of glucose to metal ions (glucose/M) on the formation of LaFeO3 was investigated. XRD analysis showed that single-phase and well-crystallized LaFeO3 was obtained from precursor with glucose/M = 3:5 and 3:10 at 500 degrees C. LaFeO3 nanoparticles with a diameter of about 30 nm were obtained. However, for precursor with glucose/M = 3:20, pure LaFeO3 was not obtained at temperature below 600 degrees C. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据