S-doped TiO2 photocatalyst with high activity of visible light was prepared by modified Sol-gel method using thiourea as sulfur source. The catalyst was characterized by XRD, FT-IR, DRS, SEM-EDX and TEM analysis. The undoped and S-doped TiO2 nanoparticles calcined at 500 degrees C contained only anatase phase. Effects of calcination temperature showed formation of rutile phase get started at 650-700 degrees C for undoped TiO2 and 750 degrees C for S-doped TiO2. The activity of the catalyst was examined by photodegradation of methyl orange in aqueous solution under both visible and UV light and it was found to be depending on the amount of S. The most activity was observed for 0.05% and 0.1% S-doped TiO2 under visible and UV light, respectively. Results showed for undoped TiO2, calcined samples at 650 and 550 degrees C under visible and UV light are the best catalysts, respectively. Also for 0.05% S-doped TiO2, calcined sample at 500 degrees C is the best catalyst under UV and visible light. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据