MATERIALS CHEMISTRY AND PHYSICS
卷 114, 期 2-3, 页码 939-942出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.matchemphys.2008.10.069
关键词
Electropolymerization; Polyaniline; Rechargeable power sources
资金
- Ministry of Science, Republic of Serbia [142044]
Polyaniline (PANI) on graphite electrode was synthesized electrochemically under galvanostatic condition at current density of 2.0 mA cm(-2) from aqueous solution of 1.0 mol dm(-3) HCl and 0.25 mol dm(-3) aniline monomer. Electrochemical characterization of the PANI electrode was performed in 0.5 mol dm(-3) HCl using cyclic voltammetry and galvanostatic measurements. The overall charge capacity of the PANI electrode was estimated to be 0.154 mAh cm(-2), which corresponds to 25% of the theoretical mass of PANI available for doping exchange. It was observed that during initial cyclization at low pH, the extent of PANI degradation products was insignificant and practically had no influence on the charge/discharge characteristics of the PANI electrode. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据