期刊
MATERIALS CHEMISTRY AND PHYSICS
卷 116, 期 2-3, 页码 631-637出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.matchemphys.2009.05.003
关键词
Amorphous materials; Intermetallics compounds; Nanostructures; Phase transitions
资金
- Ministry of Science and Higher Education [N507 057 31/1290]
Al-Fe alloys containing 60, 65, 70, 75, 80, 83 and 85 at.% of All were prepared by high-energy ball milling. Thermal behaviour of the mechanically alloyed alloys was investigated using differential scanning calorimetry. The phase transformations and structural changes taking place in the materials during milling and during subsequent heating in a calorimeter were investigated by X-ray diffraction. For the alloys with 60% and 65% of Al, a supersaturated Fe(Al) solid solution was the milling product. For the Al-30%Fe composition it was a two-phase Al5Fe2 + Fe(Al) alloy, while for the Al-25%Fe and Al-20%Fe compositions an Al5Fe2 intermetallic, at least partially ordered, was produced. All these alloys were nanocrystalline. Amorphous alloys were obtained for the compositions with 83% and 85% of Al. Heating of the milling products in the calorimeter caused transformation of the solid solution into an ordered FeAl intermetallic, formation of Al5Fe2 intermetallic for the Al-35%Fe composition and transformation of Al5Fe2 intermetallic into Al13Fe4 one in the case of the Al-20%Fe composition. Amorphous alloys crystallised upon heating yielding a mixture of Al13Fe4 intermetallic and Al. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据