TiO2 nanopowder; La-doping; STM/STS; Optical spectroscopy; Photocatalysis
类别
资金
- Serbian Ministry of Education and Science [III45018, ON171032, ON172042]
- SASA Project [F-134]
The influence of La-doping in the range of 0.5-6.0 mol% on structural and morphological properties of TiO2 nanopowders synthesized by sol-gel routine has been investigated by XRPD, AFM, EDS and BET measurements, as well as Raman spectroscopy. The XRPD and Raman measurements have revealed the anatase phase as dominant in all nanopowders, with crystallite size decreasing from similar to 15 nm in pure TiO2 to similar to 12 nm in La-doped samples. The BET data suggest that all samples are fully mesoporous, with mean pore diameters in the range of similar to 6-8 nm. The specific surface area and the complexity of pore structure are greater in doped samples than in pure TiO2 sample. The spectroscopic ellipsometry has apparently shown that the band gap has been gradually increased with the increase of La content. The STM and STS techniques have been used successfully to evaluate the surface morphology and electronic properties of La-doped nanopowders. All investigated properties have been related to photocatalytic activity, tested in degradation of a metoprolol tartrate salt (0.05 mM), and induced by UV-radiation. All doped samples showed increased photocatalytic activity compared to pure TiO2, among which the 0.65 mol% La-doped sample appeared to be the most efficient. (C) 2013 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据