期刊
MATERIALS CHARACTERIZATION
卷 84, 期 -, 页码 34-40出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.matchar.2013.07.007
关键词
Laminated composite; Magnesium alloy; Aluminum alloy; Interface; hot rolling
类别
资金
- National Natural Science Foundation of China [51175363, 51274149]
- Youth Science Foundation of Shanxi Province [2008021033]
- Fund for the Doctoral Program of Higher Education of China [20111402110004]
- Program for Changjiang Scholar and Innovative Research Team in University [IRT0972]
Using a two-pass hot rolling process, Al(5052)/Mg(AZ31)/Al(5052) alloy laminated composite plates were fabricated. The first pass was performed at relatively low temperatures, and the second pass was performed at higher temperatures. No new phases formed at the bond interface after the first hot rolling pass. High temperature annealing with the annealing temperature at or above 300 degrees C caused the formation of continuous layers of the intermetallics Mg17Al12 and Al3Mg2 at the bond interface of Al(5052)/Mg(AZ31). The growth rate of the intermetallic layers increased with increasing the annealing temperature, while the incubation time decreased with increasing the temperature. A kinetic equation was developed to describe the growth of the intermetallic compound layers. The second hot rolling pass caused the break of the continuous intermetallic layers into fragments, which were intermittently dispersed at the bond interface. (C) 2013 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据