MATERIALS CHARACTERIZATION
卷 80, 期 -, 页码 21-27出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.matchar.2013.03.009
关键词
Mg2Ni; Amorphization behavior; High energy ball-milling; Thermal stability; Hydrogenation performance
类别
资金
- Defense Industrial Technology Development Program [A2720110010]
- 111 project [B08040]
Amorphous Mg2Ni alloy was prepared by high energy ball-milling starting with polycrystalline Mg2Ni which was prepared with the help of a metallurgy method by using a SPEX 8000D mill. The microstructural and phase structure characterization of the prepared materials was performed via scanning electron microscopy, transition electron microscope and X-ray diffraction. The thermal stabilities were investigated by differential scanning calorimetry. The apparent activation energies were determined by means of the Kissinger method. The first and second crystallization reactions take place at similar to 255 degrees C and similar to 410 degrees C, and the corresponding activation energy of crystallization is Ea(1) = 276.9 and E-a2 = 382.4 kJ/mol, respectively. At 3 MPa hydrogen pressure and 250 degrees C, the hydrogen absorption capacities of crystalline, partially and fully amorphous Mg2Ni alloy are 2.0 wt.%, 3.2 wt.% and 3.5 wt.% within 30 min, respectively. (C) 2013 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据