MATERIALS CHARACTERIZATION
卷 62, 期 9, 页码 904-911出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.matchar.2011.06.008
关键词
Cu-Ni-Si alloy; Solution treatment; Aging; Precipitation; Isothermal heat treatment
类别
资金
- Nonferrous Metals Science Foundation of HNG-CSU
- Higher Educational Institutions of Hunan Province
- Hunan Provincial Innovation Foundation for Postgraduate
- Excellent Doctor Degree Thesis Support Foundation of Central South University
The transformation behavior of Cu-8.0Ni-1.8Si-0.6Sn-0.15Mg alloy during isothermal heat treatment has been studied by transmission electron microscope observation. On the basis of micro-hardness measurement, time-temperature-property curves of the alloy have been established, and nose-temperatures of curves are about 650 degrees C. Discontinuous precipitates appeared as the samples isothermal heat treated at 550 degrees C, while continuous precipitates appeared as the samples isothermal heat treated at temperatures below 550 degrees C and above 650 degrees C. (beta-Ni(3)Si, delta-Ni(2)Si and delta'-Ni(2)Si precipitates were observed in the specimens. The crystal orientation relationships between copper matrix and precipitates were determined as (0 (22) over bar)(Cu)parallel to(0 (11) over bar)(beta)parallel to(010)(delta), [100](Cu)parallel to[100](beta)parallel to[001](delta); (0 (22) over bar)(Cu)parallel to(0 (11) over bar)(beta)parallel to(100)(delta)', [100](Cu)parallel to[100](delta)'. (c) 2011 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据