MATERIALS CHARACTERIZATION
卷 61, 期 11, 页码 1097-1102出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.matchar.2010.07.003
关键词
High Cr steel; Creep crack growth; Microstructural change; Stress state
The microstructures near to and remote from the tip of a crack in ASME Gr 92 steel were investigated after creep crack growth at 873 and 898 K focusing on the martensitic lath the dislocation structure and precipitates After creep the mean lath width near the crack hp was obviously larger than that of the virgin material whereas the lath width remote from the crack tip was only slightly larger than that of the virgin material The mean dislocation density near the crack tip markedly decreased after creep whereas only a small change was observed in the dislocation density remote from the crack tip The mean size of M23C6 particles near the crack tip after creep was larger than that of the virgin material whereas their mean size remote from the crack hp was almost the same as that of the virgin material (C) 2010 Elsevier Inc All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据