期刊
MATERIALS CHARACTERIZATION
卷 61, 期 5, 页码 569-574出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.matchar.2010.02.016
关键词
Joining; Welding; Superalloy
类别
资金
- NSERC of Canada
- Standard Aero Ltd. Winnipeg Canada
- Manitoba Government
The susceptibility of pre-weld heat treated laser beam welded IN 738 superalloy to heat affected zone (HAZ) cracking was studied. A pre-weld heat treatment that produced the minimal grain boundary liquation resulted in a higher level of cracking compared to those with more intergranular liquation. This deviation from the general expectation of influence of intergranular liquation extent on HAZ microfissuring is attributable to the reduction in the ability of the base alloy to accommodate welding tensile stress that accompanied a pre-weld heat treatment condition designed to minimize intergranular liquation. Furthermore, in contrast to what has been generally reported in other nickel-based superalloys, a decrease in laser welding speed resulted in increased HAZ cracking in the IN 738, which can be attributed to exacerbated process instability at lower welding speeds. (C) 2010 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据